Enhanced green emission from UV down-converting Ce3+–Tb3+ co-activated ZnAl2O4 phosphor PROJECT TITLE :Enhanced green emission from UV down-converting Ce3+–Tb3+ co-activated ZnAl2O4 phosphorABSTRACT:Ce3+–Tb3+ co-activated ZnAl2O4 powder phosphors were prepared by a solution combustion method using urea as a fuel. X-ray diffraction characterization showed that all the powders crystallized in the well known cubic spinel phase of ZnAl2O4. An enhanced down-converted green emission associated with the 5D4→7F5 transitions of Tb3+ ions was observed at 543 nm from the ZnAl2O4:Ce3+, Tb3+ powders with different concentrations of Ce3+ and Tb3+. It was inferred from the fluorescence decay data that the enhancement was due to energy transfer from Ce3+ to Tb3+. Further, cathodoluminescence intensity degradation of the ZnAl2O4:Ce3+, Tb3+ powder phosphors was investigated when the powders were irradiated with 2 keV electrons. X-ray photoelectron spectroscopy was used to analyze the chemical and electronic states of individual elements before and after electron irradiation. The ZnAl2O4:Ce3+, Tb3+ phosphor was evaluated to be used as a UV down-converting layer in conventional silicon photovoltaic cells or as a source of green light in field emission display technologies. Did you like this research project? To get this research project Guidelines, Training and Code... Click Here facebook twitter google+ linkedin stumble pinterest Quantification of cesium surface contamination on silicon resulting from SIMS analysis UV capillary force lithography for multiscale structures